氟化物特性
氟化物 Datasheet
|
Item |
Unit |
ASTM |
PTFE(4F) 鐵弗龍 |
PFA |
PCTFE |
PVDF |
FEP |
PEEK |
|
|
Test Method |
(3F) |
(2F) |
(4-6F) |
||||||
|
|
Density |
|
D792 |
2.14~2.20 |
2.12~2.17 |
2.1~2.2 |
1.75~2.17 |
2.12~2.17 |
1.31 |
|
Melting Point |
°C |
|
327 |
302~310 |
210~212 |
170 |
253~282 |
340 |
|
|
Physical Properties 物性特質 |
Tensile
Strength |
Kg/cm² |
D638 |
280~350 |
320 |
315~420 |
400~520 |
200~320 |
1142 |
|
Elongation |
% |
D638 |
200~400 |
280~300 |
80~250 |
100~300 |
250~330 |
20 |
|
|
Compression
Strength |
Kg/cm² |
D695 |
120 |
- |
320~520 |
600 |
150 |
|
|
|
Impact
Strength |
Kg*cm/cm |
D256 |
16.3 |
Not
Damaged |
13.6~14.7 |
19.6~21.8 |
Not
Damaged |
Not
Damaged |
|
|
Hardness |
Rockwell Hardness |
D785 |
R25 |
- |
R75~95 |
R100~115 |
R25 |
R126 |
|
|
Hardness |
Shore Hardness |
D1706 |
D55 |
D60 |
D90 |
D80 |
D55 |
D85 |
|
|
Static
Friction Coefficient |
|
- |
0.05 |
- |
0.25 |
0.1 |
. |
|
|
|
Kinetic
Friction Coefficient |
|
- |
0.1 |
0.2 |
0.37 |
0.39 |
0.3 |
0.4 |
|
|
Thermal |
Heat
Conductivity |
10-4cal/cm. |
C117 |
5.9 |
6.2 |
4.7~5.3 |
3 |
6 |
|
|
sec.°C |
|||||||||
|
|
Coefficient
of Linear Expansion |
10-5 /°C |
D696 |
9.9(23~66°C) |
12(21~100°C) |
4.5~7.0 |
8.5 |
8.3~10.5 |
|
|
(-73~71°C) |
|||||||||
|
Operating
Temperature |
°C |
|
260 |
260 |
150~180 |
150 |
200 |
300 |
|
|
Electrical |
Volume
Resistibility |
Ω.cm |
D257 |
>1018 |
>1018 |
12*1018 |
20*1014 |
>1018 |
|
|
Surface
Resistibility |
Ω |
D257 |
>1016 |
>1016 |
- |
- |
>1016 |
>1013 |
|
|
|
Insulation
Resistibility |
1/8”thick |
D149 |
16~24 |
20~24 |
20~24 |
10.4 |
20~24 |
24 |
|
Kv/mm |
|||||||||
|
Durability |
Chemical
Resistance |
|
D543 |
Excellent |
Excellent |
Good |
Good |
Excellent |
Good |
|
Flammability |
% |
D635 |
Non-Flammable |
Non-Flammable |
Non-Flammable |
自行消化 |
Non-Flammable |
Flame
Resistant |
|
|
Permeability |
% |
D570 |
<0.01 |
0.03 |
0 |
0.04 |
<0.01 |
0.1 |
|
氟素樹脂的種類及耐化性比較
|
分類 (名稱) |
分子構造 (1分子中氟素含有量) |
融點及連續使用溫馨 | 耐化性 |
|
PTFE 聚四氟乙烯 Polyetrafluoroethylene
|
 |
m.p. 327oC W.TEMP(MAX) 260oC |
極優異化學安定性,對所有化學藥品及溶劑非活性,但對高溫之熔融鹼金屬,和高溫高壓下之氟素氣體及氟素化合物CIF3,OF2.等會產生活 |
|
ETFE 四氟乙唏和乙烯共聚物 Ethylene-tetra fluoroethylene |
|
m.p. 270oC W.TEMP(MAX) 150oC |
雖與PTFE的耐藥性略同，但卻容易被濃硝酸等侵蝕。 |
|
ECTFE(3F) 聚三氟氯乙烯和乙烯共聚物 Ethylene-chlorotrifluoroethylene |
|
m.p. 240oC W.TEMP(MAX) 150oC |
為較高結晶的高分子材料，具有較佳的抗滲透性。 |
|
PFA 四氟乙烯Polythtrafluoroethylene和全氟烷基乙烯基醚Perfluoroalkylvinylether之共聚物 |
|
m.p. 302~310oC W.TEMP(MAX) 260oC |
與PTFE之耐化學性相同，但潔淨度及機械強度較高。 |
|
FEP(4-6F) 四氟乙烯和六氟丙烯之共聚物 Fluorinated Ethylene Propylene |
|
m.p. 253~282oC W.TEMP(MAX) 160oC |
耐化學性接近PTFE， 但耐溫度則較低些 |
|
PVDF(2F) 聚偏二氟乙烯 Polyvinylidene Difluoride |
|
m.p. 170oC W.TEMP(MAX) 130~150oC |
對發煙硫酸、高溫濃硫酸或100°C以上的苛性蘇打等容易分解,並對丙酮、酮、二甲基、乙醯胺等類極強性的溶劑,或對於n-丁基胺等極鹼性的一級胺,亦會膨脹或溶解 |
相關產品連結
►PTFE 鐵氟龍成型加工零件
►PFA 射出接頭 PFA管
►PFA 裡襯|閥門|接頭|管配件